1. Nominal Thickness with profile SP 106-107-108-109-110. When coupled with profile SP 111, nominal thickness will be 1 mm thinner - f.i. EPQ-SP111 nominal thickness 8 (+ 1 / -0.5) 2. Only typical data for selection purpose, not to be used for part or tool design. Tab 1 Tab 2a Tab 2b Code Tensile plies Nominal1 belt thickness mm Sliding ply Working load daN/cm Working load daN/cm Recommended2 applications and characteristics Pes Cotton 1% 1,50% ELG 1 7.5 (+1/-0.5) 1 - 12 4-6 7-9 For machines with table length ≤ 1 m and with 1 tooling head. Traction power ≤ 1KW EPQ 2 9 (+1/-0.5) 1 - 20 6-8 12-14 For machines with table length ≤ 2.5 - 3 m and with 2 or 3 tooling heads. More than 1 mm for each step of calibration. Traction power ≤ 2 kW EPQP 3 10 (+1/-0.5) 1 - 30 7-9 14-16 The same as EPQ. For machines with table length > 3 m and with 3 or more tooling heads. Traction power ≤ 4.5 kW. Also suggested for machines with vacuum devices. EPQC 2 9 (+1/-0.5) - 1 20 6-8 13-15 The same as EPQ EPQPC 3 10 (+1/-0.5) - 1 28 7-9 14-16 The same as EPQP EMQC 2 12 (0/-1) - 1 20 6-8 13-15 Replaces EPQ for maximum flatness of the belt and very thin material (< 1mm). SP100 profile. EMQPC 3 13 (0/-1) - 1 28 7-9 14-16 Replaces EPQP for maximum flatness of the belt and very thin material (< 1mm). SP100 profile. SME400 1+cord 8 (+1/-0.5) - - 40 25 - For edge and shaping profile sanding machine. With V guide and width ≤ 200 mm. Producible upon request. SPECIAL RUBBER COVERS Denomination Colour Hardness °ShA ( ±5 ) Recommended2 applications and characteristics HB WHITE 65 HYPALON rubber: oil, chemical, wear and high heat resistance PA GRAY 40, 50, 60 Super grip and tear resistance NC/NCB BLACK/WHITE 65 NITRILE rubber: very good oil and abrasion resistance STANDARD RUBBER COVERS Denomination Colour Hardness °ShA ( ±5 ) Recommended2 applications and characteristics CB GREY 40, 50, 60, 70 General purposes. Excellent impact strength and tear resistance, good machinability during surfacing, when using the sanding belt belonging to the machine outfit. Excellent grip to prevent slipping of the materials being machined. High compression strain. CS BLACK 57 The same as for CB with particular tendency to limit antistatic charges; keep down the accumulation of dust particles on the belt surface